Qiming Machinery supplies the following material to cast your ball mill liner: Manganese Steel. The manganese content of the high manganese steel ball mill lining plate is generally 11-14%, and the carbon content is generally 0.90-1.50%, most of which are above 1.0%. At low impact loads, the hardness can reach HB300-400.
Liner, Mill Liner, Ball Mill Liner manufacturer / supplier in China, offering High Manganese Steel/Rubber/Alumina Ball Mill Liner Plates, Iron Ore, Lime Stone, Phosphate Rock Stone Jaw Crusher, PE Jaw Crusher for Stone, Quarry, Mining, Construction Crushing and so on.
High Manganese Steel Castings- This is a unique alloy which is used in manufacturing of Ball Mill Liner, and Manganese Liners. It has high durability, malleability, high work hardening capacity is non-magnetic in nature and typically great protection from wear.
Mn13, Mn13Cr2 and Mn18Cr2 steel casting liners for Cement Mill / Ball Mill Liners. 2. Appliion: It is applicable to the working condition of strong impact, such as teeth plates, concaves and mantles of c. 3. Microstructure: Austenite or Austenite + little Carbide. 4. Hardness: Less than HB300. 5. Impact Value: more than 118J. 6.
Ball mill liners from MGS Casting maximize the lifespan and performance of your ball mill, with a selection of rubber and rubber composite liners available. Refined through ongoing design improvements, our ball mill liners maximize uptime and service intervals while providing an improved crushing of the ore.
Manganese Steel Casting Parts. Qiming Machinery a manganese steel casting foundry,which had focused on this area over 30 years. Every year, our foundry casted more than 12,000 tons manganese steel casting parts.
End liners for ball mills conform to the slope the mill head and can be made of high chrome steel. and hardness, this steel widely used in casting mill liners for Why use manganese steel to cast mill liners? Manganese steel, also called Hadfield steel or mangalloy, is a steel alloy containing 12-14% manganese.
The ball mill liner has a strong ability to lift the grinding body. Most of them will be cast with high manganese steel, because high manganese steel has strong impact resistance and the surface can Cold work hardens and becomes hard and abrasion resistant.
Under low impact load, Manganese Steel Ball Mill Liner can achieve HB300~400, Under high impact load, can achieve HB500~800. Different impact load, the Manganese Steel Ball Mill Liner''s surface hardening layer depth can be up to 10~20 mm. High hardness of hardening layer can resist the wear of
The ball mill main wear parts is ball mill liner and steel balls. We can offer ball mill liner OEM casting according to spare parts drawings. If possible, we can also send engineers to customer site for spare parts mapping!It is a high technological enterprise that integrated research ,
It states that the high manganese steel liner plate when is in use, especially in medium and small sized ball mills, fails to fully play its anti-abrasion. Moreover, the yield strength of the high manganese steel liner plate is relatively low, so it is easy to have the plastic deformation, making the liner plate bulge or may even snap the construction bolt to have the liner plate be difficult
High Manganese Steel Casting Sag Mill Liners High Hardness for Industry . Summarization . High Cr white iron material possess a coination of superior abrasion resistance and a reasonable . degree of toughness. The high Cr castings have longer service life than the other material,such as
The mill liner cost must include installation downtime and bolts, gaskets cost. Ore hardness will affect the metal choice. Hard ore will work harden the manganese steel, using steel ball as a Grinding Media, can make manganese steel harden sufficiently even if the ore is soft.
High manganese steel ball mill liner can be used for ball mill, crushers, loaders, excavators, Cutting tools, bulldozers, digging bucket and knife plate, screw conveyor and other wear-resistant structural parts production equipment, by gas cutting processing and various welding, despite the steel sheet with high strength , but cold bending performance well, it can be cold forming.